TYPICAL PROPERTIES OF TOYOLAC 100 322 Typical Properties Test Method Test Conditions SI Unit Typical Value Physical Specific Gravity ASTM D792 - 1.04 o Water Absorption ASTM D570 23 C x 24 hours % 0.3 Mould Shrinkage ASTM D955 % 0.4 ~ 0.6 Rheological Melt Flow Rate ISO 1133 220oC / 10 kg g/10 min 15 Mechanical Tensile stress at yield ASTM D638 at 5 mm/min MPa 48 Tensile strain at break ASTM D638 at 5 mm/min % 48 Flexural Strength ASTM D790 at 3 mm/min MPa 74 Flexural Modulus ASTM D790 at 3 mm/min MPa ...
40, Yeongudanji-ro, Ochang-eup, Cheongwon-gun, Chungcheongbuk-do, TEL 82-43-211-6144 FAX 82-43-211-6148 363-883 Rep. of KOREA Report No : TAC-003235 Receipt Date : Jul.24.2015 Client : HAN MYEUNG HO Test Completion Date : Aug.06.2015 Hanwha L&C 78F, CENTER1 Bldg, 26, Uljiro 5-gil, Jung-gu, Seoul, Korea Sample : Scagliola(HANEX) D-2 TEST RESULTS TEST ITEM UNIT SAMPLE RESULT TEST METHOD Specific Gravity((23/23) ) - - 1.760 ASTM D792-13(Method A) Rockwell Hardness(HRM) - - 88 ASTM D785-08(Procedure A) Tensile Strength MPa - 39.4 ASTM D638-14(*) Tensile Modulus of GPa - 10.8 ASTM D638-10(*) Elasticity Flexural Strength MPa ...
6Chemical Properties 61 Rate of Water and Moisture Absorption The rate of water absorption is ASTMD570after 24 hours in water 0. 23~0. 26 The rate of water and moisture absorption of Iupilon / NOVAREX is as shown in Fig. 611. in boiling water rate of water absorption (%) in room temperature water in atmosphere time (hr) Fig. 611 Water absorption curve of Iupilon / NOVAREX (ASTM-D570) Also, the rate of water absorption measured according to JISK6771-1958 was After 24 hours in 50ˆwater 0.29% After 24 hours in 75ˆwater 0.39% This method of measuring the rate of ...
PDF | 0.10 MB | Free Download